Analisi degli effetti del processo di laser powder bed fusion applicato ad acciai con diverso contenuto di carbonio.

In this thesis work, steel samples with different carbon content and the effects due to their manufacturing process are presented, specifically these are C67 and 316L samples made using Laser Powder Bed Fusion (L-PBF). By analyzing the porosity, microstructure and hardness, a global study of the samples is carried out, allowing the comparison of the different results obtained in the two steels. The objective of the paper is to highlight the advantages or disadvantages due to Additive Manufacturing processes. The analysis performed on C67 samples made with AM processes is innovative as they are commonly produced through rolling, drawing and extrusion processes.

In questo lavoro di tesi si presentano dei campioni in acciaio con diverso contenuto di carbonio e gli effetti dovuti al loro processo di realizzazione, nello specifico si tratta di campioni in C67 e 316L realizzati tramite Laser Powder Bed Fusion (L-PBF). Analizzando la porosità, la microstruttura e la durezza si effettua uno studio globale dei campioni, consentendo il confronto dei diversi risultati ottenuti nei due acciai. L’obiettivo dell’elaborato è mettere in luce i vantaggi o gli svantaggi dovuti a processi di Additive Manufacturing. Innovativa è l’analisi eseguita sui campioni in C67 realizzati con processi AM in quanto comunemente prodotti mediante processi di laminazione, trafilatura ed estrusione.